Solid Surfaces Materials
Solid Surfaces are typically used in households,
office buildings and industry places where the
materials can be incorporated as kitchen and
bathroom countertop, display and bar settings,
boardroom meeting tables, lighting boxes, sinks and
basins, and even shelves. Composed from resins
and aluminium trihydrate (ATH), Solid Surfaces are
non-toxic and retardant to flames which made it
deemed the most suitable material for most interior
design.
Solid Surfaces Materials
Its non-porous and stain-resistant characteristics compel Solid Surfaces into a perfect choice
for various environments, especially the kitchen and bathroom where the surfaces are always
open to bacteria and dirt. Solid Surfaces are low maintenance materials where any blemishes
such stain can be removed with soap water; cuts and scrapes can be removed by sanding or
mild abrasives so that the surface would look brand new again.

Solid Surfaces are available in a wide range of choices from meteoroid to diamond, jewel to
translucent, even pearl-effect - a total of more than 100 varieties. We also provide them in
almost any shapes required to complement your interior. Whether you are integrating it with
porcelain, copper or glass,
YAXIS® Solid Surfaces can be integrated into your interior
seamlessly for the appealing and pleasant look.

Why choose YAXIS® Solid Surfaces?

  • It's non-porous, non-toxic and safe for use.
  • It's durable and easy to maintain.
  • It's thermoformable and hygienic.
  • It can be integrated into your design seamlessly.
  • It's the material of choice for industry designers and architects.
  • It comes in a wide range of patterns, textures and colours.
Specifications
Most of our Solid Surfaces comes in a standard size of 762mm x 3048mm with a thickness of 12mm, which can be
customised according to design upon the installation process. However, customisation of colours would require a minimum
quantity order. Kindly refer to the specifications of YAXIS® Solid Surfaces below.
Standard Size
762mm x 3048mm (12mm thickness) *Sizes can be customised according to design
upon installation.
Colors
Standard colours as presented in our catalogue and website. Customisation of
colours available based on a minimum quantity order.
Finishing
Available finishing options:
  • Matte (up to #400 grit sandpaper is required)
  • Semi Gloss (up to #600 - #800 grit sandpaper is required)
  • Gloss (up to #1000 - #1500 grit sandpaper is required)
Thermoforming
Achievable at temperature of 80°C - 120°C.
Joint Adhesive
Provided upon purchase of YAXIS® Solid Surfaces
Warranty
  • 10-year limited warranty
  • Free one-time polish during the first 18 months after installation
YAXIS® Solid Surfaces
Certified & Test Proven by Sirim Malaysia - Report No.: PTC/ER09/370
No
Property
Result
Test Method
1
Specific Gravity
1.770
ASTM D 792
2
Izod Impact Strength
(notched), J/m
18.5
ASTM D 256
Pendulum: 2 Joule
3
Tensile Strength, MPa
26.6
ASTM D 638
Crosshead Speed: 5 mm/minute
Initial Gauge length: 50 mm
Specimens: Dumbbell Type I
 
Elongation at Break,%
0.3
 
 
Tensile Modulus, MPa
8,720
 
4
Flexural Strength, MPa
49.4
ASTM D 790 Crosshead
Speed: 5.5 mm/minute Support
Span: 208 mm
 
Flexural Modulus, MPa
10,700
 
5
Water Absorption (24 hour
immersion), %
0.01
ASTM D 570
6
Rockwell Hardness
93
ASTM D 785
7
Barcol Hardness
63
ASTM D 258
8
Point Impact
No sign of fracture was observed when a
polished steel ball of 1 ?inches in diameter was
dropped from a height of 610 mm on each of
four different areas on the test
specimen(Comply)
ICPA-SS-1 Clause 4.1
9
Knife Drop
No sign of cracks or fractures were observed.
(Comply) The unit shall not show any cracks or
fractures. Any damage shall not extend through
the surface finish and shall be restorable to
approximate the original finish by using
abrasives and polishing compounds
ANSI Z124.6.4.2.2
10
Skillet Drop
No sign of cracks or fractures were observed.
(Comply) The unit shall not show any cracks or
fractures
ANSI Z124.6.4.2.3
11
Cigarette Burn
Non-ignition.No damage was observed.
(Comply) There shall be no ignition or
progressive glow of the surface during or after
contacted with the lighted cigarette
ANSI Z124.6.5.4
12
Heated Pan
No cracking, crazing, discolouration or
blistering were observed. (Comply) = 0.5
There shall be no cracking, crazing,
discolouration or blistering. Any discolouration
shall be removable using abrasives and
polishing compound to approximate the original
finish and serviceability.The average colour
difference shall be no more than ±2 CIE units
ANSI Z124.6.5.6